Plasma display unit, phosphor and process for producing phosphor

ABSTRACT

A plasma display device having suppressed luminance degradation of a phosphor, a suppressed change in chromaticity and improved discharge characteristics as a result of suppression of adsorption of water or hydrocarbon-containing gas on the surface of the blue phosphor. A blue phosphor layer used in the plasma display device is formed of a compound expressed by Ba 1-X MgAl 10 O 17 :Eu X  or Ba 1-x-y Sr y MgAl 10 O 17 :Eu X  and includes at least one element that is selected from Nb, Ta, Pr, P, As, Sb, Bi and Tm and substitutes for a part of its Al or Mg element.

TECHNICAL FIELD

[0001] The present invention relates to a plasma display device used as, for example, a television for image display and also relates to a phosphor and a method of manufacturing the phosphor.

BACKGROUND ART

[0002] Of color display devices used as, for example, computers and televisions for image display, a display device using a plasma display panel (hereinafter referred to as “PDP”) has received attention in recent years as a large-size, thin and lightweight color display device.

[0003] The plasma display device using this PDP produces a display in full color by additive mixture of so-called three primary colors (red, green and blue). For display in full color, the plasma display device is provided with phosphor layers which emit respective lights having the respective three primary colors, that is, red (R), green (G) and blue (B). Phosphor particles of each phosphor layer are excited by ultraviolet rays generated in a discharge cell of the PDP, thereby producing visible colored light.

[0004] Known compounds used for the above-described phosphors having the respective colors include (YGd)BO₃:Eu³⁺ which emits the red light, Zn₂SiO₄:Mn²⁺ which emits the green light and BaMgAl₁₀O₁₇:Eu²⁺ which emits the blue light. Each of these phosphors is made by mixing specified raw materials and then firing a resulting mixture at a high temperature of at least 1,000° C. for solid-phase reaction (refer to, for example, “Phosphor Handbook” published by Ohmsha, Ltd., pp. 219 and 225). The phosphor particles obtained by this firing are ground and sifted before use (so that the red and green phosphor particles have a mean particle diameter of 2 μm to 5 μm, while the blue phosphor particles have a mean particle diameter of 3 μm to 10 μm). The phosphor particles are ground and sifted (classified) for the following reason. In general, paste including the phosphor particles having each color is applied by screen printing to form the phosphor layer in the PDP. The surface of the paste applied easily becomes smoother if the particle diameters of the phosphor are smaller and more uniform (in particle size distribution). In other words, the smaller and the more uniform the particle diameters of the phosphor and the more spherical the phosphor particles, the smoother the applied surface. Accordingly, packing density and a light-emitting surface area of the phosphor particles in the phosphor layer conceivably increase, thus increasing luminance of the plasma display device.

[0005] However, reducing the particle diameters of the phosphor particles increases the surface area of the phosphor and thus increases the number of defects in the phosphor. For this reason, a large amount of water, carbon dioxide or hydrocarbon-containing organic substances easily adheres to the surface of the phosphor. For a blue phosphor, including a divalent Eu ion as a luminescence center, such as Ba_(1-x)MgAl₁₀O₁₇:Eu_(x) or Ba_(1-x-y)Sr_(y)MgAl₁₀O₁₇:Eu_(x), in particular, its crystal structure has a layer structure (refer to, for example, “Display and Imaging”, 1999, Vol. 7, pp. 225-234). This layer structure includes an oxygen (O) vacancy in the vicinity of a layer (Ba—O layer) including a Ba atom, and the smaller the particle diameters, the more these vacancies problematically increase in number (refer to, for example, “OYO BUTSURI (Applied Physics)”, Vol. 70, No. 3, 2001, p. 310). FIG. 6 schematically illustrates the structure of the Ba—O layer of the blue phosphor, Ba_(1-X)MgAl₁₀O₁₇:Eu_(X).

[0006] For the above reason, water existing in the air or hydrocarbon-containing gas selectively adsorbs on the surface of such a Ba—O layer. Such water and gas are released into the panel in large amounts in a panel manufacturing process and react with the phosphor and MgO during discharge, thus problematically degrading the luminance, causing a change in chromaticity (which leads to a color shift or a burn on a screen), reducing a drive margin and raising discharge voltage.

[0007] It is also known that the defects increase further in number as vacuum ultraviolet rays (VUV), having a wavelength of 147 nm, and which are generated by discharge in driving the panel, are absorbed, thus problematically degrading the luminance of the phosphor further (refer to, for example, “Technical Report” published by the Institute of Electronics, Information and Communication Engineers, EID99-94, Jan. 27, 2000).

[0008] To solve these problems, the following conventional method (such as disclosed in Japanese Patent Unexamined Publication No. 2001-55567) is devised. According to this method, the whole surface of a phosphor is covered with a crystal coating of Al₂O₃ for the purpose of repairing the vacancy in the vicinity of the Ba—O layer.

[0009] However, covering the whole surface of the phosphor with the crystal coating of Al₂O₃ causes the ultraviolet rays to be absorbed, thus problematically reducing the emission luminance of the phosphor.

[0010] In view of the problems discussed above, the present invention aims to suppress degradation of luminance of a phosphor or a change in chromaticity, or improve discharge characteristics by suppressing adsorption of water on the surface of the blue phosphor.

DISCLOSURE OF THE INVENTION

[0011] To address the problems discussed above, a plasma display device constructed according to the present invention includes a plasma display panel including a plurality of disposed discharge cells having one of one color and a respective plurality of colors, and disposed phosphor layers that have respective colors corresponding to the respective discharge cells and are excited by ultraviolet rays to emit light, wherein the phosphor layers includes a blue phosphor, the blue phosphor is formed of a compound expressed by one of Ba_(1-x)MgAl₁₀O₁₇:Eu_(x) and Ba_(1-x-y)Sr_(y)MgAl₁₀O₁₇:Eu_(x), and the compound includes at least one element, selected from Nb, Ta, Pr, P, As, Sb, Bi and Tm, for substituting for a part of one of an Al element and a Mg element.

[0012] In such a structure, the pentavalent element is substituted for the part of the aluminum (Al) element or magnesium (Mg) element in the blue phosphor, thus reducing oxygen vacancies in the vicinity of Ba—O layers and suppressing adsorption of water or hydrocarbon-containing gas on a surface of the blue phosphor. Consequently, degradation of luminance of the panel or a change in chromaticity is suppressed, or discharge characteristics are improved without a decrease in luminance of the phosphor.

BRIEF DESCRIPTION OF THE DRAWINGS

[0013]FIG. 1 is a plan view of a PDP in accordance with an exemplary embodiment of the present invention, schematically illustrating an arrangement of electrodes of the PDP.

[0014]FIG. 2 is a sectional view in perspective, illustrating a structure of an image display region of the PDP in accordance with the embodiment of this invention.

[0015]FIG. 3 is a drive block diagram of a plasma display device in accordance with the embodiment of this invention.

[0016]FIG. 4 is a sectional view illustrating the structure of the image display region of the PDP in accordance with the embodiment of this invention.

[0017]FIG. 5 is a schematic diagram illustrating a structure of an ink applying device used in forming a phosphor layer of the PDP in accordance with the embodiment of this invention.

[0018]FIG. 6 is a schematic view illustrating an atomic structure of a blue phosphor in accordance with the embodiment of this invention.

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENT

[0019] An exemplary embodiment of the present invention is demonstrated hereinafter with reference to the accompanying drawings.

[0020] Inventors of this invention have found that degradation of luminance is caused essentially not by the existence of a defect, but selective adsorption of water, carbon dioxide or hydrocarbon-containing gas to the oxygen (O) vacancy in the vicinity of a Ba—O layer. A phosphor reacts with the adsorbing water or hydrocarbon under irradiation with ultraviolet rays or ions, thus causing the luminance degradation or a color shift. In other words, the inventors have come to know that various degradations are caused by the adsorption of water, carbon dioxide or hydrocarbon-containing gas to the oxygen vacancy in the vicinity of the Ba—O layer in the blue phosphor.

[0021] Based on such knowledge, the degradations, which occur when a panel is manufactured and driven, have been prevented by reducing the oxygen vacancies in the vicinity of the Ba—O layers of the blue phosphor without a decrease in luminance of the blue phosphor. The oxygen vacancies in the vicinity of the Ba—O layers could be reduced by substituting a pentavalent element for a part of an aluminum (Al) element or a magnesium (Mg) element of a blue phosphor having a crystal structure, such as BaMgAl₁₀O₁₇:Eu or BaSrMgAl₁₀O₁₇:Eu.

[0022] A description is provided hereinafter of an advantage of the substitution of the pentavalent ion for the part of the Al or Mg element in BaMgAl₁₀O₁₇.

[0023] In the blue phosphor, BaMgAl₁₀O₁₇:Eu, Al and Mg are present as trivalent and divalent positive ions, respectively. Substituting the pentavalent positive ion, such as niobium (Nb), tantalum (Ta), praseodymium (Pr), phosphorus (P), arsenic (As), antimony (Sb), bismuth (Bi) or thulium (Tm), for Al or Mg increases the number of positive charges in the crystal. To neutralize or compensate for the positive charge, oxygen carrying a negative charge fills the oxygen vacancy in the vicinity of the Ba element. As a result, the oxygen vacancies in the vicinity of the Ba—O layers can conceivably be reduced.

[0024] A description is provided hereinafter of methods of manufacturing the phosphor of a plasma display device of the present invention.

[0025] Conceivable methods of manufacturing the phosphor-include a solid-phase reaction method using a material, such as an oxide, a nitrate or a carboxide, and flux, a liquid phase method of heat-treating a precursor of the phosphor that is made by hydrolyzing organometallic salts or nitrates in an aqueous solution or made by a coprecipitation method of adding an alkali or the like for precipitation, and a liquid spray method of spraying an aqueous solution including phosphor materials into a heated furnace. Even when the phosphor is made by any of these methods, the substitution of the pentavalent ion (Nb, Ta, Pr, P, As, Sb, Bi or Tm) for the part of the Al or Mg element in BaMgAl₁₀O₁₇:Eu has been discovered to be effective.

[0026] A description is provided now of preparation of the blue phosphor by the solid-phase reaction method. Materials including the carboxides, such as BaCO₃ and MgCO₃, and the oxides, such as Al₂O₃, Eu₂O₃ and M₂O₅ (where M is Nb, Ta, Pr, P, As, Sb, Bi or Tm) are mixed with a small amount of flux (AlF₃ or BaCl₂), which is a sintering accelerator. A resulting mixture is fired at 1,400° C. for about 2 hours and then ground and sifted. Next, the mixture ground and sifted is fired at 1,500° C. for about 2 hours in a reducing atmosphere (including 5% of H2 and N₂) and thereafter ground and sifted again, thus forming the phosphor.

[0027] Firing this phosphor further in an oxidizing atmosphere is effective in preventing the luminance degradation or generation of the defect in the phosphor that is caused by vacuum ultraviolet rays (VUV) during discharge (driving).

[0028] Preparation of the phosphor by the liquid phase method is as follows. The organometallic salts (e.g. alkoxides or acetylacetone) or the nitrates that include the elements forming the phosphor are dissolved in water for hydrolysis, thus forming a co-precipitate (hydrate). Next, the hydrate is subjected to hydrothermal synthesis in an autoclave for crystallization, firing in air or sprayed into a high-temperature furnace, thus forming fine phosphor particles. The fine phosphor particles are fired at 1,500° C. in a reducing atmosphere (including 5% of H₂ and N₂) and then ground and sifted.

[0029] It is desirable that the pentavalent ion (Nb, Ta, Pr, P, As, Sb, Bi or Tm) in an amount of 0.01% to 3% be substituted for Al or Mg. The substitution amount of less than 0.01% is less effective in preventing the luminance degradation, and the substitution amount of more than 3% results in reduced luminance of the phosphor. The above-described pentavalent ion is substituted for the Al or Mg ion, not the Ba or Eu ion because it has been confirmed that the blue phosphor has a wavelength of 450 nm in an emission spectrum regardless of the amount of substitution.

[0030] The amount of substitution of the pentavalent element (Nb, TA, Pr, P, As, Sb, Bi or Tm) for the Al or Mg element is as follows. When Ba(Mg_(1-a)Ma)(Al_(1-b)Mb)₁₀O₁₇:Eu_(x), it is preferable that 0.0001≦a≦0.01, and 0.0001≦b≦0.01. In other words, the substitution amount preferably ranges from 0.01% to 3% inclusive.

[0031] The blue phosphor thus made has small particle diameters ranging from 0.05 μm to 3 μm and has a favorable particle size distribution. If the phosphor particles forming a phosphor layer are spherical in shape, packing density increases further, thus substantially increasing a light-emitting area of the phosphor particles that contributes to light emission. Accordingly, the luminance of the plasma display device increases, and consequently, the plasma display device obtained can have excellent luminance characteristics with the luminance degradation and the color shift suppressed.

[0032] It is more preferable that the phosphor particles have a mean particle diameter of 0.1 μm to 2.0 μm. Also, it is more preferable that the particle size distribution is such that the maximum particle diameter is at most four times the mean particle diameter, while the minimum particle diameter is at least one quarter of the mean particle diameter. The ultraviolet rays reach to a depth as shallow as hundreds of nanometers from the surface of the phosphor particles, and substantially only the surface of the phosphor particles emits light. With the phosphor particles having diameters up to 2.0 μm, the surface area of the particles that contributes to the light emission increases, so that the phosphor layer maintains high luminous efficiency. With the particle diameters not less than 3.0 μm, the phosphor layer needs to have a thickness of at least 20 μm, so that enough discharge space cannot be secured. With the particle diameters not more than 0.1 μm, the defect is prone to occur, so that the luminance does not improve. If the thickness of the phosphor layer is 8 to 25 times the mean particle diameter of the phosphor particles, enough discharge space can be secured, while the phosphor layer maintains high luminous efficiency.

[0033] Concrete phosphor particles used for the blue phosphor layer in the plasma display device of the present invention use a compound expressed by Ba_(1-x)MgAl₁₀O₁₇:Eu_(x) or Ba_(1-x-y)Sr_(y)MgAl₁₀O₁₇:Eu_(x). When values X and Y in the compound are such that 0.03≦X≦0.20 and 0.1≦Y≦00.5, the luminance increases further, which situation is preferable.

[0034] Concrete phosphor particles used for a red phosphor layer in the plasma display device of this invention use a compound expressed by Y_(2-X)O₃:Eu_(X) or (Y,Gd)_(1-X)BO₃:Eu_(X). When value X in the compound is such that 0.05≦X≦0.20, the red phosphor exhibits excellent luminance and resistance to degradation of luminance, which situation is preferable.

[0035] Concrete phosphor particles used for a green phosphor layer in the plasma display device of this invention use a compound expressed by Ba_(1-X)Al₁₂O₁₉:Mn_(X) or Zn_(2-X)SiO₄:Mn_(X). When value X in the compound is such that 0.01≦X≦0.10, the green phosphor exhibits excellent luminance and resistance to luminance degradation, which situation is preferable.

[0036] Referring to the accompanying drawings, a description is provided hereinafter of the plasma display device in accordance with the exemplary embodiment of the present invention.

[0037]FIG. 1 is a plan view of the PDP, schematically illustrating an arrangement of electrodes, and FIG. 2 is a perspective view illustrating an image display region of the PDP. In FIG. 1, the numbers of display electrodes, display scan electrodes and address electrodes are reduced to facilitate the description.

[0038] As shown in FIG. 1, PDP 100 includes front glass substrate 101 (not shown), rear glass substrate 102, N display electrodes 103, N display scan electrodes 104 (the Nth electrode is denoted by N), M address electrodes 107 (the Mth electrode is denoted by M) and hermetically sealing layer 121 designated by a shaded part. This PDP 100 has an electrode matrix having a three-electrode structure including electrodes 103, 104, 107. Cells are formed where address electrodes 107 intersect display electrodes 103 and display scan electrodes 104. Image display region 123 is formed inwardly of hermetically sealing layer 121

[0039] As shown in FIG. 2, PDP 100 is constructed as follows. A front panel, which includes display electrodes 103, display scan electrodes 104, dielectric glass layer 105 and MgO protective layer 106 disposed above a principal surface of its front glass substrate 101, and a rear panel, which includes address electrodes 107, dielectric glass layer 108, barrier ribs 109 and phosphor layers 110R, 110G, 110B disposed above a principal surface of its rear glass substrate 102, are put together, and discharge space 122 formed between the front and rear panels is filled with discharge gas. FIG. 3 is a block diagram illustrating the structure of the plasma display device including a driving circuit.

[0040] As shown in FIG. 3, PDP 100 is provided with display driver circuit 153, display scan driver circuit 154 and address driver circuit 155. Under control of controller 152, a voltage is applied to display scan electrode 104 and address electrode 107 of the cell to be illuminated for address discharge between these electrodes 104, 107. Thereafter, a pulse voltage is applied between display electrode 103 and display scan electrode 104 for sustain discharge, from which the ultraviolet rays are generated in the above-mentioned cell. Phosphor layer 107 excited by the ultraviolet rays emits the light, thus illuminating the cell. An image is displayed by a combination of the illuminated and unilluminated cells having the respective colors.

[0041] Referring to FIGS. 4 and 5, a description is provided next of a method of manufacturing the above-mentioned PDP. FIG. 4 is a sectional view of the PDP, and FIG. 5 is a sectional view of a phosphor ink applying device.

[0042] The front panel is formed in the following manner. First, N display electrodes 103 and N display scan electrodes 104 (FIG. 2 shows only two electrodes 103 and two electrodes 104) are alternately formed in parallel relation like stripes on front glass substrate 101. Subsequently, these electrodes 103, 104 are covered with dielectric glass layer 105, which is then covered with MgO protective layer 106.

[0043] Display electrode 103 and display scan electrode 104 are each formed of a transparent electrode made of ITO and a bus electrode made of silver and are formed by firing subsequent to application of silver paste for the bus electrodes through screen printing.

[0044] Dielectric glass layer 105 is formed to have a specified thickness (approx. 20 μm) by applying paste including lead glass material through screen printing and then firing the paste at a specified temperature (e.g. 560° C.) for a specified period of time (e.g. 20 minutes). Examples of the paste including the lead glass material for use include a mixture of PbO (70 wt %), B₂O₃ (15 wt %), SiO₂ (10 wt %), Al₂O₃ (5 wt %), and an organic binder made by dissolving 10% of ethyl cellulose in α-terpineol. The organic binder mentioned here includes resin dissolved in an organic solvent. Instead of ethyl cellulose, acrylic resin can be used as the resin, and butyl carbitol or the like can be used as the organic solvent. Further, a dispersant such as glyceryltriloleate may be mixed into such an organic binder.

[0045] MgO protective layer 106 is made of magnesium oxide (MgO) and is formed by, for example, sputtering or chemical vapor deposition (CVD) to have a specified thickness (about 0.5 μm).

[0046] The rear panel is formed in the following manner. First, M address electrodes 107 are formed in rows by applying silver paste for these electrodes to rear glass substrate 102 through screen printing or photolithography, and then firing the paste. Subsequently, dielectric glass layer 108 is formed on these electrodes 107 by applying paste including lead glass material through screen printing. Thereafter, barrier ribs 109 are formed by repeatedly applying the same paste including the lead glass material to dielectric glass layer 108 at specified pitches through screen printing and then firing the paste. These barrier ribs 109 partition discharge space 122 into the cells (unit light-emitting regions) along the rows.

[0047]FIG. 4 is a partially sectional view of PDP 100. As shown in FIG. 4, interval W between barrier ribs 109 is conditioned to range from about 130 μm to 240 μm in accordance with a HDTV with a diagonal screen of 32 inches to 50 inches. The red (R), green (G) and blue (B) phosphors are each applied to a groove between barrier ribs 109. In the blue (B) phosphor, Ba_(1-X)MgAl₁₀O₁₇:Eu_(X) or Ba_(1-x-y)Sr_(y)MgAl₁₀O₁₇:Eu_(X), the pentavalent element is substituted for the part of the Al or Mg element. Paste-like phosphor ink including each of these phosphors and an organic binder is applied and fired at a temperature of 400° C. to 590° C., whereby the organic binder is burnt out. In this way, phosphor layers 110R, 110G, 110B each having the phosphor particles bound are formed. It is desirable that thickness L of each of these phosphor layers 110R, 110G, 110B along the direction of lamination be about 8 to 25 times the mean particle diameter of the phosphor particles above address electrode 107. In other words, it is desirable that the phosphor layer has such a thickness that the phosphor particles are stacked to form at least 8 layers, preferably about 20 layers. This is because, instead of permitting passage of the ultraviolet rays, the phosphor layer needs to absorb the ultraviolet rays generated in discharge space 122 for ensuring the luminance (luminous efficiency) when irradiated with a certain amount of ultraviolet rays. With a more thickness, the luminous efficiency of phosphor layers 110R, 110G, 110B becomes almost saturated. With a thickness exceeding the thickness of about 20 layers, sufficiently large discharge space 122 cannot be secured. Even when the numbers of layers stacked are the same, phosphor particles having sufficiently small particle diameters and spherical shapes, like those obtained by hydrothermal synthesis or the like are packed more densely in a phosphor layer and have a larger total surface area than particles which are not spherical in shape. For this reason, these phosphor particles increase the surface area contributing to actual light emission of the phosphor layer, thus increasing the luminous efficiency. Synthesis methods for these phosphor layers 110R, 110G, 110B, and a method of manufacturing blue phosphor particles including trivalent Eu ions substituting for 15% to 75% of divalent Eu ions for use in a blue phosphor layer are described later.

[0048] The front and rear panels thus made are placed one on top of the other with address electrodes 107 of the rear panel orthogonal to electrodes 103, 104 of the front panel. Sealing glass is disposed along a periphery of the panels and fired, for example, at 450° C. for 10 to 20 minutes to form hermetically sealing layer 121 (see FIG. 1) for sealing. Subsequently, discharge space 122 is once exhausted of air to a high vacuum (e.g. 1.1×10⁻⁴ Pa) and then filled with the discharge gas (e.g. He—Xe or Ne—Xe inert gas) at a specified pressure, thus completing PDP 100.

[0049]FIG. 5 is a schematic diagram illustrating a structure of the ink coating apparatus used in forming the phosphor layer. As shown in FIG. 5, ink coating apparatus 200 includes server 210, pressurizing pump 220 and header 230. By being pressurized by pressurizing pump 220, the phosphor ink is supplied from server 210, which stores the phosphor ink, to header 230. Header 230 has ink chamber 230 a and nozzle 240 (having an inside diameter of 30 μm to 120 μm). The phosphor ink supplied to ink chamber 230 a by pressurization is discharged continuously from nozzle 240. It is desirable that bore diameter D of nozzle 240 be at least 30 μm to prevent the nozzle from clogging up and at most interval W (ranging from about 130 μm to 200 μm) between barrier ribs 109 for preventing the applied ink from extending over the barrier ribs. Typically, bore diameter D is set at 30 μm to 130 μm.

[0050] Header 230 is constructed to be driven linearly by a header scanning mechanism (not shown). Allowing header 230 to scan with nozzle 240 discharging phosphor ink 250 continuously allows the phosphor ink to be applied uniformly to the groove between barrier ribs 109 over rear glass substrate 102. The phosphor ink used here has a viscosity kept in a range of 1,500 to 30,000 centipoises (CP) at 25° C.

[0051] Server 210 is provided with an stirring apparatus (not shown), which prevents precipitation of the particles in the phosphor ink by stirring. Header 230 is integrally formed to include ink chamber 230 a and nozzle 240 and is made by performing machining and electric discharge machining on metallic material.

[0052] The method of forming the phosphor layers is not limited to the method described above. Other various kinds of methods usable include photolithography, screen printing and a method of disposing a film including the phosphor particles mixed therein.

[0053] The phosphor particles having each color, the binder and an organic solvent are mixed to form the 1,500- to 30,000-centipoise (CP) phosphor ink. On an as needed basis, a surface active agent, silica, a dispersant (0.1 to 5 wt %) or the like may be added.

[0054] Ethyl cellulose or acrylic resin can be used as the binder included in the phosphor ink (to account for 0.1 to 10 wt % of the ink), and α-terpineol or butyl carbitol can be used as the solvent. A polymer, such as PMA or PVA, can also be used as the binder, and an organic solvent, such as diethylene glycol or methyl ether, can also be used as the solvent.

EMBODIED EXAMPLES

[0055] A description is provided hereinafter of the synthesis methods for the respective phosphors used in the present embodiment.

[0056] First, a description is provided of the blue phosphor, Ba_(1-X)MgAl₁₀O₁₇:Eu_(X), synthesized by hydrothermal synthesis.

[0057] In a process of preparing a mixed solution, materials including barium nitrate (Ba(NO₃)₂), magnesium nitrate (Mg(NO₃)₂), aluminum nitrate (Al(NO₃)₃) and europium (Eu(NO₃)₂) are mixed in a molar ratio of 1-X:1:10:X (where 0.03≦X≦0.2) and dissolved in an aqueous medium, whereby the hydrated mixed solution is made. As the aqueous medium, ion-exchange water or pure water is preferable because either water contains no impurities. However, the aqueous medium can be used even when a non-aqueous solution, such as methanol or ethanol, is also included.

[0058] As a material for substituting the pentavalent ion (Nb, Ta, Pr, P, As, Sb, Bi or Tm) for Mg or Al, a nitrate, a chloride or an organic compound that includes the above-mentioned pentavalent ion is used. The amount of substitution is as follows. When (Mg_(1-a)Ma)(Al_(1-b)Mb) (where M is the pentavalent ion), the material is mixed so that 0.0001≦a≦0.03, and 0.0001≦b≦0.03.

[0059] Next, the hydrated mixed solution is poured in a container made of corrosion- and heat-resistant material, such as gold or platinum and then undergoes hydrothermal synthesis in a device capable of heating and pressurizing simultaneously, such as the autoclave, for 12 to 20 hours at a specified temperature (100° C. to 350° C.) under a specified pressure (0.2 MPa to 25 MPa), thus forming fine phosphor particles.

[0060] Subsequently, the particles are fired in a reducing atmosphere (including, for example, 5% of hydrogen and 95% of nitrogen) at a specified temperature (e.g. 1,350° C. to 1,600° C.) for a specified period of time (e.g. 2 hours) and then classified. Consequently, the desired blue phosphor, Ba_(1-x)MgAl₁₀O₁₇:Eu_(x), including the pentavalent ion substituting for the part of Mg or Al can be obtained. To increase resistance to the vacuum ultraviolet rays (VUV), this phosphor may be fired in an oxidizing atmosphere (at a temperature of preferably 700° C. to 1,000° C.).

[0061] The phosphor particles obtained by such hydrothermal synthesis are spherical in shape and have particle diameters smaller than those of particles made by conventional solid-phase reaction (with a mean particle diameter of about 0.05 μm to 2.0 μm). The term “spherical” used here is defined because most of the phosphor particles have aspect ratios (minor axis diameter/major axis diameter) ranging, for example, between 0.9 and 1.0 inclusive. However, not all the phosphor particles need to have aspect ratios falling within this range.

[0062] The blue phosphor can be obtained even when the hydrated mixed solution prepared in the above-mentioned mixed solution preparation process is sprayed from a nozzle into the high-temperature furnace.

[0063] A description is provided next of the blue phosphor, Ba_(1-x-y)Sr_(y)MgAl₁₀O₁₇:Eu_(x), made by solid-phase reaction.

[0064] Materials including barium hydroxide (Ba(OH)₂), strontium hydroxide (Sr(OH)₂), magnesium hydroxide (Mg(OH)₂), aluminum hydroxide (Al(OH)₃) and europium hydroxide (Eu(OH)₂) undergo weighing so that a required molar ratio is obtained. Next, an oxide or a hydroxide that includes the pentavalent ion (Nb, Ta, Pr, P, As, Sb, Bi or Tm) which substitutes for Mg or Al undergoes weighing so that a required ratio is obtained. These materials are mixed with flux, AlF₃. A resulting mixture is fired at a specified temperature (1,300° C. to 1,400° C.) for a specified period of time (12 to 20 hours), whereby Ba_(1-x-y)Sr_(y)MgAl₁₀O₁₇:Eu_(x) including the pentavalent ion substituting for Mg or Al can be obtained.

[0065] Next, this Ba_(1-x-y)Sr_(y)MgAl₁₀O₁₇:Eu_(x) is fired in a reducing atmosphere (including, for example, 5% of hydrogen and 95% of nitrogen) at a specified temperature (1,000° C. to 1,600° C.) for 2 hours and thereafter classified, whereby the phosphor can be obtained. The materials used for the phosphors mainly include the oxide, the nitrate and the hydroxide. However, an organometallic compound, including an element such as Ba, Sr, Mg, Al, Eu, Nb, Ta, Pr, P, As, Sb, Bi or Tm, such as a metal alkoxide or acetylacetone, can be used for forming the phosphors. If the above-mentioned reduced phosphor is annealed in an oxidizing atmosphere, a resulting phosphor degrades less from the VUV.

[0066] A description is provided next of the green phosphor, Zn_(2-X)SiO₄:Mn_(X).

[0067] In a first process of preparing a mixed solution, materials including zinc nitrate (Zn(NO₃)), silicon nitrate (Si(NO₃)₂) and manganese nitrate (Mn(NO₃)₂) are mixed in a molar ratio of 2-X:1:X (where 0.01≦X≦0.10). Next, this mixed solution is sprayed from a nozzle into the high-temperature furnace heated to 1,500° C. with ultrasonic waves applied. In this way, the green phosphor is made.

[0068] A description is provided next of the green phosphor, Ba_(1-X)Al₁₂O₁₉:Mn_(X).

[0069] In a first process of preparing a mixed solution, materials including barium nitrate (Ba(NO₃)₂), aluminum nitrate (Al(NO₃)₂) and manganese nitrate (Mn(NO₃)₂) are mixed in a molar ratio of 1-X:12:X (where 0.01≦X≦0.10) and then dissolved in ion-exchange water, whereby the mixed solution is made. In a hydration process, a basic aqueous solution (e.g. aqueous ammonia solution) is dropped into this mixed solution, whereby a hydrate is made. In a hydrothermal synthesis process, this hydrate and ion-exchange water are poured in a capsule made of corrosion- and heat-resistant material, such as platinum or gold and then undergo hydrothermal synthesis in a high-pressure vessel such as the autoclave at a specified temperature (e.g. 100° C. to 300° C.) under a specified pressure (e.g. 0.2 MPa to 10 MPa) for a specified period of time (e.g. 2 to 20 hours). Thereafter, drying is carried out, whereby desired Ba_(1-X)Al₁₂O₁₉:Mn_(X) is obtained. A phosphor obtained by this hydrothermal synthesis process has particle diameters of about 0.1 μm to 2.0 μm and are spherical in shape. Next, these fine particles are annealed in air at a temperature of 800° C. to 1,100° C. and then classified, whereby the green phosphor is obtained.

[0070] A description is provided next of the red phosphor, (Y,Gd)_(1-X)BO₃:Eu_(X).

[0071] In a process of preparing a mixed solution, materials including yttrium nitrate (Y₂(NO₃)₃), gadolinium hydronitrate (Gd₂(NO₃)₃), boric acid (H₃BO₃) and europium nitrate (Eu₂(NO₃)₃) are mixed in a molar ratio of 1-X:2:X (where 0.05≦X≦0.20, and the Y-to-Gd ratio is 65:35).

[0072] Next, this mixed solution is heat-treated in air at a temperature of 1,200° C. to 1,350° C. for 2 hours and then classified, whereby the red phosphor is obtained.

[0073] A description is provided next of the red phosphor, Y_(2-X)O₃:Eu_(X). In a process of preparing a mixed solution, materials including yttorium nitrate (Y₂(NO₃)₂) and europium nitrate (Eu(NO₃)₂) are mixed in a molar ratio of 2-X:X (where 0.05≦X≦0.30) and then dissolved in ion-exchange water, whereby the mixed solution is made. In a hydration process, a basic aqueous solution (e.g. aqueous ammonia solution) is added to this mixed solution, whereby a hydrate is made. In a hydrothermal synthesis process, this hydrate and ion-exchange water are poured in a container made of corrosion- and heat-resistant material such as platinum or gold and then undergo hydrothermal synthesis in a high-pressure vessel such as the autoclave, for example, at a temperature of 100° C. to 300° C. under a pressure of 0.2 MPa to 10 MPa for 3 to 12 hours. A resulting compound is thereafter dried, whereby fine red phosphor particles are made. Next, these phosphor particles are annealed in air at a temperature of 1,300° C. to 1,400° C. for 2 hours and then classified, whereby the red phosphor is obtained. The phosphor obtained by this hydrothermal synthesis process has particle diameters of about 0.1 μm to 2.0 μm and are spherical in shape. These particle diameters and shapes are suitable for formation of a phosphor layer having excellent light-emitting characteristics.

[0074] The phosphors used for respective phosphor layers 110R, 110G of above-mentioned PDP 100 are conventional phosphors, while phosphor layer 110B uses the above-mentioned phosphor particles including the pentavalent ion substituting for the part of Mg or Al of the phosphor. For a conventional blue phosphor, degradation in each process is severer than that of the blue phosphor of the present invention, so that color temperature of white tends to decrease when the lights having the respective three colors are emitted at the same time. For this reason, the color temperature of white display has been improved by reducing luminance of cells having the respective red and green phosphors through use of a circuit in a plasma display device. However, the use of the above-mentioned blue phosphor increases the luminance of the blue cell and reduces degradation during panel production, thus eliminating the need for intentional reduction of the luminance of the cells having the other colors. Since the luminances of all the colored cells can thus be used to the full, the luminance of the plasma display device can be increased, while the color temperature of the white display is kept high.

[0075] The blue phosphor of the present invention can find application in a fluorescent lamp where this phosphor emits light in a similar manner by being excited by ultraviolet rays. In this case, conventional blue phosphor particles to be applied to an inner wall of a fluorescent tube are replaced with the phosphor layer made of the blue phosphor including the pentavalent ion substituting for the part of Mg or Al of the phosphor. Application of the present invention to the fluorescent lamp in such a manner can afford luminance and resistance to degradation of the luminance that are more excellent than those of the conventional fluorescent lamp.

[0076] For performance evaluation of the plasma display device of the present invention, phosphor samples based on the above-described embodiment and plasma display devices using the respective samples were made, and performance evaluation of the devices was conducted as follows.

[0077] Each plasma display device has a diagonal screen of 42 inches (which is within specifications of a HDTV having a rib pitch of 150 μm) and was made to include a 20-μm-thick dielectric glass layer, a 0.5-em-thick MgO protective layer and a distance of 0.08 mm between a display electrode and a display scan electrode. A discharge space is filled with discharge gas, which is a gas mixture including mainly neon and 5% of xenon gas, at a specified discharge gas pressure.

[0078] Conditions of synthesis and specifications for each phosphor sample are shown in Table 1. A phosphor used as blue phosphor particles used in each of the plasma display devices corresponding to respective samples 1-10 in Table 1 includes a pentavalent ion substituting for a part of Mg or Al of the phosphor. Samples 4, 6 and 8 had their respective blue phosphors annealed in an oxidizing atmosphere (including N₂ and O₂) at 700° C., 900° C., 1,000° C., respectively, for 2 hours after synthesis. TABLE 1 Blue Phosphor (Ba_(1-x)MgAl₁₀O₁₇:Eu_(x)) Pentavalent Element Substituting for Al or Mg and Red Phosphor Green Phosphor Amount (%) of ((Y, Gd)_(1-x)BO₃:Eu_(x)) ((Zn_(2-x)Mn_(x))₂SiO₄) Sample Amount Manufacturing Pentavalent Amount (x) Manufacturing Amount (x) Manufacturing No. (x) of Eu Method Element of Eu Method of Mn Method 1 x = 0.03 Hydrothermal Nb 0.05% x = 0.1 Solid-Phase Reaction x = 0.01 Spray Method Synthesis Method Method 2 x = 0.05 Solid-Phase Reaction Ta 0.01% x = 0.2 Spray Method x = 0.02 Hydrothermal Method (Flux Method) Synthesis Method 3 x = 0.1 Spray Method Pr 0.03% x = 0.3 Aqueous Solution x = 0.05 Solid-Phase Reaction Method Method 4 x = 0.2 Aqueous Solution P 3.0% x = 0.15 Hydrothermal x = 0.1 Solid-Phase Reaction Method and Firing at Synthesis Method Method 700° C. in N₂—O₂ Atmosphere Blue Phosphor (Ba_(1-x-y)Sr_(y)MgAl₁₀O₁₇:Eu_(x)) Pentavalent Element Substituting for Al or Mg and Amount Red Phosphor Green Phosphor Amounts (%) of ((Y_(1-x))₂O₃:Eu_(x)) (Ba_(1-x)Al₁₂O₁₉:Mn_(x)) Sample (x, y) of Pentavalent Amount (x) Manufacturing Amount (x) of Manufacturing No. Eu and Sr Manufacturing Method Element Eu Method of Mn Method 5 x = 0.03 Solid-Phase Reaction As 1.0% x = 0.01 Hydrothermal x = 0.01 Hydrothermal y = 0.1 Method (Flux Method) Synthesis Method Synthesis Method 6 x = 0.1 Hydrothermal Sb 0.05% x = 0.1 Spray Method x = 0.02 Spray Method y = 0.3 Synthesis Method and Firing at 900° C. in N₂—O₂ Atmosphere 7 x = 0.1 Spray Method Bi 0.02% x = 0.15 Aqueous Solution x = 0.05 Solid-Phase y = 0.5 Method Reaction Method 8 x = 0.2 Solid-Phase Reaction Tm 1.0% x = 0.2 Solid-Phase Reaction x = 0.1 Solid-Phase y = 0.3 Method and Firing at Method Reaction Method 1,000° C. in N₂—O₂ Atmosphere 9 x = 0.2 Solid-Phase Reaction P 1.0% x = 0.2 Solid-Phase Reaction x = 0.1 Solid-Phase y = 0.3 Method and Firing at Pr 0.5% Method Reaction Method 1,000° C. in N₂—O₂ Atmosphere 10 x = 0.1 Solid-Phase Reaction P 0.5% x = 0.15 Aqueous Solution x = 0.01 Hydrothermal y = 0.5 Method and Firing at Tm 0.1% Method Synthesis Method 1,000° C. in N₂—O₂ Atmosphere 11* x = 0.1 Solid-Phase Reaction No Pentavalent x = 0.15 Aqueous Solution x = 0.01 Hydrothermal y = 0.5 Method Element Method Synthesis Method

[0079] Samples 1-4 each use a combination of (Y,Gd)_(1-X)BO₃:Eu_(X) (red phosphor), Zn_(2-X)SiO₄:Mn_(X) (green phosphor) and Ba_(1-X)MgAl₁₀O₁₇:Eu_(X) (blue phosphor). The synthesis method for the phosphor, the pentavalent ion substituting for Mg or Al, the amount of pentavalent ion, and the substitution ratios of Eu and Mn, which become luminescence centers, that is, the substitution ratio of Eu to the Y element, the substitution ratio of Eu to the Ba element and the substitution ratio of Mn to the Zn element are varied as shown in Table 1.

[0080] Samples 5-10 each use a combination of Y_(2-X)O₃:Eu_(X) (red phosphor), Ba_(1-X)Al₁₂O₁₉:Mn_(X) (green phosphor) and Ba_(1-x-y)Sr_(y)MgAl₁₀O₁₇:Eu_(X) (blue phosphor). Similarly to the above, the conditions of the synthesis method for the phosphor, the pentavalent ion substituting for Mg or Al ion of the blue phosphor, the amount of pentavalent ion, and the substitution ratios of the luminescence centers are varied as shown in Table 1.

[0081] Phosphor ink used for forming a phosphor layer in formation of a PDP uses each of those kinds of phosphor particles shown in Table 1 and was made by mixing the phosphor, resin, a solvent and a dispersant. Each phosphor ink thus made has a viscosity kept in a range of 1,500 CP to 30,000 CP at 25° C. When each phosphor layer formed was observed, the phosphor ink was applied uniformly to each wall surface of each barrier rib. The phosphor particles used for the phosphor layer having each color have a mean particle diameter of 0.1 μm to 3.0 μm and a maximum particle diameter not more than 8 μm.

[0082] Comparative sample 11 is a sample using conventional blue phosphor particles which did not undergo any specific substitution.

[0083] (Experiment 1)

[0084] Luminance of the blue color of each of samples 1-10 and comparative sample 11 made was measured before as well as after the phosphor was fired (at 520° C. for 20 minutes) in a process of manufacturing a rear panel, and a luminance degradation rate of the blue color was determined. Specifically, the luminance of the phosphor particles was measured before firing, and the luminance of the ink applied and fired was measured.

[0085] (Experiment 2)

[0086] A change of luminance of each blue phosphor between before and after the panels were put together and sealed (at 450° C. for 20 minutes) was determined in manufacture of the PDP.

[0087] (Experiment 3)

[0088] Luminance was measured before as well as after the PDP was illuminated with blue light, and a luminance degradation rate was determined. Specifically, the luminance of the panel was measured before as well as after discharge sustain pulses of 100 kHz were applied to each plasma display device at 200 V for 100 straight hours, and the luminance degradation rate (<[the luminance after the application−the luminance before the application]/the luminance before the application>*100) was determined from these measurements.

[0089] Addressing failure in address discharge was determined by presence of a flicker in an image. Even one flicker is counted as the addressing failure.

[0090] Table 2 shows the luminances and the luminance degradation rates of each color as results of these experiments 1-3.

[0091] As shown in Table 2, comparative sample 11 using the blue phosphor not including the substituent pentavalent ion has a high luminance degradation rate in each step. This comparative example 11 has a 5.5% decrease in luminance after the phosphor firing step, a 21.5% decrease in luminance after the sealing step and a 35% decrease in luminance in the accelerated life test carried out at 200 V and 100 kHz. Samples 1-10 each have a blue color degradation rate lower than 3% and no addressing failure.

[0092] This is because the oxygen vacancies in the blue phosphor (especially the oxygen vacancies in the vicinity of the Ba—O layers) were reduced substantially by the substitution of the pentavalent ion (Nb, Ta, Pr, P, As, Sb, Bi or Tm) for the part of the Mg or Al element of the blue phosphor. Accordingly, water existing in the atmosphere or given off by the MgO layer, the barrier rib, the sealing frit, the phosphor and others conceivably did not adsorb on the defective layers (the oxygen vacancies in the vicinity of the Ba—O layers) at the surface of the phosphor in firing of the phosphor and in sealing of the panels.

[0093] Samples 4, 6 and 8, which had their respective blue phosphors annealed in the oxidizing atmosphere, had their oxygen vacancies reduced and accordingly have reduced luminance degradation rates in the test where the discharge sustain pulses of 100 kHz were applied at 200 V. TABLE 2 Luminance Luminance Luminance Degradation Degradation Degradation Rate (%) Rate (%) Rate (%) of of Phosphor of Phosphor Phosphor After Fired After Discharge at 520° C. Panels were Sustain Pulses in Rear Put Together of 100 kHz Luminance of Panel and were Applied Addressing Blue Display Manufacturing Sealed at 200 V Failure in over Whole Sample Process at 450° C. for 100 hrs Address Surface No. Blue Red Green Blue Red Green Blue Red Green Discharge cd/cm² 1 −0.3 −1.2 −4.9 −2.1 −2.6 −13.0 −2.0 −4.4 −14.5 Absent 83.2 2 −0.5 −1.3 −4.0 −1.9 −2.4 −13.2 −2.0 −4.1 −14.2 Absent 83.5 3 −0.2 −1.4 −4.5 −2.2 −2.3 −12.9 −2.2 −4.0 −14.6 Absent 85.5 4 −0.1 −1.4 −4.7 −0.4 −2.2 −12.7 −0.5 −4.2 −14.1 Absent 80.4 5 −0.2 −1.5 −4.9 −2.0 −2.0 −12.9 −2.1 4.3 −14.8 Absent 88.1 6 −0.4 −1.2 −4.3 −0.6 −2.3 −12.6 −0.8 −4.1 −14.9 Absent 88.5 7 −0.4 −1.4 −4.5 −1.8 −2.4 −12.3 −2.0 −4.2 −14.7 Absent 89.5 8 −0.1 −1.2 −4.3 −0.4 −2.5 −12.5 −0.3 −4.3 −15.1 Absent 82.5 9 −0.3 −1.5 −4.1 −1.6 −2.1 −12.8 −1.8 −4.1 −15.6 Absent 90.2 10  −0.2 −1.3 −4.2 −1.5 −2.3 −13.0 −1.5 −4.1 −14.8 Absent 87.5 11* −5.5 −1.5 −4.1 −21.5 −2.1 −13.2 −35 −4.1 −15.6 Present 45.8

[0094] (Experiment 4)

[0095] In a model experiment, these samples were left in an atmosphere having a relative humidity of 90% at 60° C. for 10 minutes and then dried at 100° C. Thereafter, these samples underwent temperature-programmed desorption-gas chromatography-mass spectrometry (TDS analysis). As a result, a water physisorption peak (around 100° C.) and a water chemisorption peak (300° C. to 500° C.) of sample 11 which has not undergone the substitution were each ten times as high as the corresponding peak of each of samples 1-10.

[0096] (Experiment 5)

[0097] In Experiment 1, the blue phosphors of the present invention have been used in the respective plasma display devices. A sample fluorescent lamp using the phosphor of this invention that emits light in a similar by being excited by ultraviolet rays in this fluorescent lamp was made. Sample fluorescent lamp 12 was made by applying a mixture, including a colored phosphor made under the conditions of sample 7 of Table 1, to an inner wall of a fluorescent tube to form a phosphor layer in a publicly known fluorescent lamp. As a comparative example, sample fluorescent lamp 13 was made by applying a mixture including the colored phosphor of sample 11 of Table 1 that was made by conventional solid-phase reaction. Table 3 shows results. TABLE 3 Luminance Degradation Sample Luminance Rate after 5,000 No. Phosphor (cd/m²) hours (100 V, 60 Hz) 12 Phosphor of Sample 7 6758 −0.95%  13* Phosphor of Sample 11 6600 −14.6%

[0098] As is clear from the results of Table 3, the phosphor of the present invention has a low luminance degradation rate even when used in the fluorescent lamp.

INDUSTRIAL APPLICABILITY

[0099] According to the present invention described above, phosphor layers include a blue phosphor layer. This blue phosphor layer is formed of a compound expressed by Ba_(1-X)MgAl₁₀O₁₇:Eu_(X) or Ba_(1-x-y)Sr_(y)MgAl₁₀O₁₇:Eu_(X), and at least one element selected from Nb, Ta, Pr, P, As, Sb, Bi and Tm is substituted for a part of an Al or Mg element of this phosphor, so that degradations in various processes for the phosphor layer can be prevented. Consequently, a PDP or a fluorescent lamp can have improved luminance, life and reliability. 

1. A plasma display device including a plasma display panel including a plurality of disposed discharge cells having one of one color and a respective plurality of colors, and disposed phosphor layers that have respective colors corresponding to the respective discharge cells and are excited by ultraviolet rays to emit light, wherein the phosphor layers include a blue phosphor, the blue phosphor is formed of a compound expressed by one of Ba_(1-x)MgAl₁₀O₁₇:Eu_(x) and Ba_(1-x-y)Sr_(y)MgAl₁₀O₁₇:Eu_(x), and the compound includes at least one element, selected from Nb, Ta, Pr, P, As, Sb, Bi and Tm, for substituting for a part of one of an Al element and a Mg element.
 2. A blue phosphor that is excited by ultraviolet rays to emit visible light and formed of a crystal structure of one of Ba_(1-x)MgAl₁₀O₁₇:Eu_(x) and Ba_(1-x-y)Sr_(y)MgAl₁₀O₁₇:Eu_(x), wherein a pentavalent element is substituted for one of an Al element and a Mg element of the phosphor.
 3. The phosphor of claim 2, wherein the pentavalent elements include at least one of Nb, Ta, Pr, P, As, Sb, Bi and Tm.
 4. The phosphor of claim 2, wherein the pentavalent element in an amount of 0.01% to 3.0% is substituted for the one of the Al and Mg elements.
 5. A method of manufacturing a phosphor, comprising: a mixed solution preparation step of mixing, to make a mixed solution, an aqueous medium and one of metal salt and organometallic salt that includes elements including, to form a blue phosphor, Ba, Mg, Al, Eu and M, where M is one of Nb, Ta, Pr, P, As, Sb, Bi and Tm; and a step of drying the mixed solution and then firing the mixed solution at a temperature of 1,000° C. to 1,500° C. in a reducing atmosphere to make a Ba_(1-x)(Mg_(1-a)Ma)(Al_(1-b)Mb)Al₁₀O₁₇:Eu_(x) phosphor and a Ba_(1-x-y)Sr_(y)(Mg_(1-a)Ma)(Al_(1-b)Mb)Al₁₀O₁₇:Eu_(x) phosphor, where Ma and Mb are each one of Nb, Ta, Pr, P, As, Sb, Bi and Tm.
 6. A method of manufacturing a phosphor, comprising: a mixed solution preparation step of mixing, to make a mixed solution, an aqueous medium and one of metal salt and organometallic salt that includes elements including, to form a blue phosphor, Ba, Mg, Al, Eu and M, where M is one of Nb, Ta, Pr, P, As, Sb, Bi and Tm; a step of drying the mixed solution and then firing the mixed solution at a temperature of 1,000° C. to 1,500° C. in a reducing atmosphere to make a Ba_(1-x)(Mg_(1-a)Ma)(Al_(l-b)Mb)Al₁₀O₁₇:Eu_(x) phosphor and a Ba_(1-x-y)Sr_(y)(Mg_(1-a)Ma)(Al_(1-b)Mb)Al₁₀O₁₇:Eu_(x) phosphor, where Ma and Mb are each one of Nb, Ta, Pr, P, As, Sb, Bi and Tm; and a step of firing the phosphors at a temperature of 700° C. to 1,000° C. in an oxidizing atmosphere after the reduction.
 7. A method of manufacturing a phosphor, comprising: a mixed solution preparation step of mixing a material and an aqueous medium to make a mixed solution; a precursor preparation step of mixing the mixed solution and a basic aqueous solution to make a hydrate which is a precursor of one of a Ba_(1-x)MgAl₁₀O₁₇:Eu_(x) phosphor and a Ba_(1-x-y)Sr_(y)MgAl₁₀O₁₇ phosphor that includes a pentavalent element substituting for one of a Mg element and an Al element; a hydrothermal synthesis step of subjecting a mixed solution including the precursor and alkali water to hydrothermal synthesis reaction at a temperature of 100° C. to 350° C. under a pressure of 0.2 MPa to 25 MPa; a step of annealing a blue phosphor obtained in the hydrothermal synthesis step at a temperature of 1,350° C. to 1,600° C. in an atmosphere including nitrogen and hydrogen; and a step of classifying a blue phosphor obtained in the annealing step. 